Fig. 4
From: Layer-by-layer self-assembly of pillared two-dimensional multilayers
Electromechanical properties of (MXene/TAEA)n multilayers. a Normalized resistance R/R0 (R0 = 1.63 kΩ) as a function of bending radius and b cyclic stability with a bending radius of 5 mm of (MXene/TAEA)10 on PET sheet. Inset in b shows a digital photograph of (MXene/TAEA)20 on PET sheet under bending condition with a LED connection. c Sheet resistances of (MXene/TAEA)n on nonwovens at flat and the knotted conditions. Inset shows a digital photograph of knotted (MXene/TAEA)30 on nonwoven with a LED connection. d Normalized resistance R/R0 (R0 = 36.2 kΩ) as a function of compressive strain for the (MXene/TAEA)6 on melamine foams, and the inset shows a photograph of the compression/resistance measurement for (MXene/TAEA)n on foams in uncompressed and with 80% compressive strain