Table 1 The values of \(\bar{{C}}\) for different crystallographic plane

From: Dislocation exhaustion and ultra-hardening of nanograined metals by phase transformation at grain boundaries

hkl

Screw

Edge

Half screw + half edge

110

0.08619

0.17472

0.1305

220

0.26

0.256

0.258

211

0.08619

0.17472

0.1305

220

0.08619

0.17472

0.1305

310

0.1974

0.2267

0.21205