Table 1 Physical and Mechanical Properties of different samples
From: In-situ forming dynamic covalently crosslinked nanofibers with one-pot closed-loop recyclability
Samples | Crosslinker Loadings (%)[a] | dav (nm)[b] | Sq[c] | Porosity (%) | WCA (°) [d] | Tensile strength (MPa) | Young modulus (MPa) | Elongation at break (%) |
|---|---|---|---|---|---|---|---|---|
DCCNF-30C | 30% | 404 ± 84 | 635 | 69.2 ± 2.3 | 118.6 ± 5.5 | 2.50 ± 0.24 | 52.5 ± 4.6 | 5.9 ± 0.8 |
DCCNF-60C | 60% | 339 ± 71 | 583 | 75.5 ± 4.1 | 129.0 ± 3.7 | 3.15 ± 0.15 | 79.2 ± 2.8 | 5.1 ± 0.3 |
DCCNF-100C | 100% | 419 ± 69 | 603 | 82.7 ± 2.5 | 129.4 ± 6.7 | 2.87 ± 0.08 | 118.5 ± 1.0 | 3.8 ± 0.2 |