Fig. 3: Environmental adaptability and stability of PUAO-50.
From: Locking small solvents by hypercrosslinked polymers towards sterically hindered organogels
a Compressive strength of PUAO-50 after curing at several typical temperatures for different times. b Image displaying the underwater injection and rapid solidification of PUAO-50. c Compressive strength of PUAO-50 after curing under different water conditions for different times. d Images of pressure stability test of PUAO-50. e Mass changes of PUAO-50 after being subjected to varying pressures for 1 h. f Mass variations and (g) compressive curves of PUAO-50 samples maintained at different temperatures for 24 h. h Mass variations and i compressive curves of PUAO-50 samples after placing in different media for 24 h. The centre of error bars and the error bars respectively correspond to the mean value and standard deviation of 3–6 measurements for each analysis.