Table 1 Compatibility of active slip systems between adjacent α and β grains in α–β Ti alloys adhering to the Burgers orientation relationship
From: Oxygen-mediated high uniform plasticity in α-β titanium alloys
Slip systems in the α-phase | Slip systems in the β-phase | Luster-Morris factor m’ a (0 ≤ m’ ≤ 1) |
|---|---|---|
(0001)<a> | {110} < 111> | 1 |
{112} < 111> | 0.87 | |
{123} < 111> | 0.94 | |
{10\(\bar{{{\bf{1}}}}\)0}<a> | {110} < 111> | 0.87 |
{112} < 111> | 1 | |
{123} < 111> | 0.98 | |
{10\(\bar{{{\bf{1}}}}\)1}<a> | {110} < 111> | 1 |
{112} < 111> | 0.88 | |
{123} < 111> | 0.95 | |
{11\(\bar{{{\bf{2}}}}\)2}<c + a > | {110} < 111> | 0.90 |
{112} < 111> | 0.99 | |
{123} < 111> | 0.99 |