Table 2 Results of the inverse prediction using the present work and conditional random search.

From: A neural network model for high entropy alloy design

 

HEA1

HEA2

C (at%)

0

0

Al (at%)

6.1

5.2

V (at%)

12.2

21

Cr (at%)

4.1

1.8

Mn (at%)

0

0

Fe (at%)

0

3.5

Co (at%)

30.6

37.3

Ni (at%)

38.8

27

Cu (at%)

0

0

Mo (at%)

8.2

4.2

Homogenization temp. (˚C)

1200

1200

Reduction rate (%)

80

80

Annealing temp. (˚C)

900

900

Annealing time (Hour)

0.25

0.25

Predicted YS (MPa)

873

819

Predicted UTS (MPa)

1297

1258