Fig. 13: Pitting mechanisms for different alloy samples during potentiodynamic polarization in 3.5 wt. % NaCl.
From: Corrosion behavior of TiZrHfBeCu(Ni) high-entropy bulk metallic glasses in 3.5 wt. % NaCl
a TCN and b Vit1.
Fig. 13: Pitting mechanisms for different alloy samples during potentiodynamic polarization in 3.5 wt. % NaCl. | npj Materials Degradation