Fig. 4: KAM maps under different fatigue cycles.
From: Improvement of stress corrosion cracking resistance by low cycle fatigue of a CrNiMoV steel
The local misorientation distribution at different fatigue cycles are presented from (a) to (e). Panel (f) shows more severe small local misorientation among grains with the increasing of fatigue cycles.