Fig. 5
From: Improvement of stress corrosion cracking resistance by low cycle fatigue of a CrNiMoV steel
Stress-strain curves with different levels of fatigue damage in 3.5% NaCl solution and air at 180 °C.
Fig. 5 | npj Materials Degradation
From: Improvement of stress corrosion cracking resistance by low cycle fatigue of a CrNiMoV steel
Stress-strain curves with different levels of fatigue damage in 3.5% NaCl solution and air at 180 °C.