Fig. 1: Cross-sectional morphology of tin bronze/steel.

Original: a SEM, b line scan result at point 1 (penetration crack) in a, c line scan result at point 2 (interface) in a in b, d–f element distribution maps; after aluminum plating: g SEM, h–k element distribution maps, l line scan results at point 3 (interface) in g.