Abstract
The synthesis of different metal oxide nanoparticles (NPs) (e.g., ZnO, MgO and SiO2) using green methods is a promising alternative to traditional chemical methods. In this work, ZnO, MgO, and SiO2 NPs were prepared using lemon peel extract. The synthesized NPs were characterized using Fourier transform infrared spectroscopy, UV–Visible spectroscopy, X-ray diffraction, and transmission electron microscopy. Also, the effects of the green synthesis of different NPs on the irrigation water quality, the availability of some heavy metals in soil and plants, and the productivity of Origanum majorana (marjoram) were studied in detail. The obtained results showed that the addition of the NPs resulted in noticeable variations in the removal percentages of Cu2+ and Fe3+ from aqueous solutions. The maximum values obtained for the adsorption of Cu(II) on ZnO, MgO, and SiO2 NPs within the pH values of 3–5 were 89.9%, 83.3%, and 68.36%, respectively. Meanwhile, the maximum adsorption values of Fe(III) at pH 3.3 were 82%, 80%, and 65% for ZnO, MgO, and SiO2 NPs, respectively. Clearly, the application of the NPs effectively reduced the available Cu2+ in the studied soil samples in the following order: Zn2 > Zn1 > Mg2 > Si2 > Mg1 > Si1 > C (control). The highest values of available Cu2+ were observed in the control treatment, whereas the lowest values were obtained when Zn2 was added. The same tendencies were observed with substantial concentrations of Fe. The addition of NPs to the soil samples positively affected the plants' Cu2+ uptake. The effects of NPs and the additions of Cu2+ and Fe3+ on the availability of nitrogen, phosphorus, and potassium (NPK) in the soil system were very completed and osculated from one treatment to another. The same tendencies were observed with the total concentration of NPK in plants.
Similar content being viewed by others
Introduction
Recently, different studies in various fields of interest have been focused on enhancing the use of different materials on very small scales close to those of molecules and atoms. Generally, 1 nm is calculated as one billionth of a meter and is considered approximately ten times the diameter of a hydrogen atom. It is known that at nanometer sizes, the chemistry and physics of materials are not expected to be appropriate. These include the reactivity, strength, color, and conductivity of materials, which substantially differ between nanoscales and largescales1,2. In the past years, the field of green chemistry has been a great area of interest, particularly in the context of a continuous energy crisis. Nanoscience may be the appropriate field in this dimension as it enables many biochemical, chemical, and biophysical transformations through reliable and easy means3. Thus, the green synthesis of ZnO, MgO, and SiO2 NPs has been exploited in several fields such as cancer treatment4, environmental remediation5, environmental and biomedical field applications6,7, transportation, food safety, environmental science, sustainable energy, medicine, and catalysis8.
In farming, nanotechnology has been exploited as a potential solution for reshaping farming construction. This could be done by replacing traditional materials used for farming construction such as pesticides, herbicides, and fertilizers with their nanoscale counterparts. Such nanoscale materials have been applied to several agricultural practices (e.g., soil foliar applications) and for grain and leafy plants8,9. Also, researchers adopt green technologies in preparing different nanoparticles (NPs) for medicinal uses in response to the increased demand for environmentally friendly NPs10. Chemical synthesis processes such as chemical vapor deposition, micellization, sol–gel formation, chemical precipitation, pyrolysis, hydrothermal methods, and others frequently result in poisonous chemicals adsorbed on surfaces, which might have negative consequences in medical applications. Some reactions necessitate high temperatures and/or high pressures to start, whereas others require inert atmospheres and/or the use of toxic substances such as H2S, toxic templates and stabilizers, and metallic precursors11. Moreover, the chemicals utilized in the formation and stabilization of NPs are hazardous and produce non-ecofriendly byproducts12. Thus, biological processes involving microbes, plants, and plant extracts have been proposed as viable alternatives to chemical procedures for preparing ZnO, MgO, and SiO2 NPs.
ZnO, MgO, and SiO2 NPs have been synthesized using various biological systems comprising bacteria, fungi, and yeasts6,8,13. Microorganism-supported NP manufacturing entails complex processes involving cell culture maintenance, intracellular synthesis, and numerous purification processes. In this regard, because standard chemical procedures are costly and necessitate the use of chemical mixes/organic solutions that act as plummeting agents, adopting “green” approaches in manufacturing zinc oxide NPs has developed into a growing area of interest14.
Several materials utilized as fertilizers are considered nanomaterials, including nano-CaO, nano-urea, nano-hydroxyapatite (nano-HAP), Mg NPs, and MgO NPs. These are considered the most widespread macronutrients reported for improving biomass construction and plant expansion. For instance, studies that used nano-HAP and nano-Mg reported increases in seed yield production for soybean (Glycine max) and cowpea (Vigna unguiculata). The study of Liu and Lal15 reported augmented growth (32.6%) and yield (20.4%) of soybean vegetation when soils were modified using nano-HAP (21.8 mg l−1). In contrast, when the vegetation was exposed to the same concentration of Ca(H2PO4)2 as the main source of phosphorous, the obtained values were moderately small. The study presented by Aziz et al.16 showed that synthesized composites with different concentrations of nitrogen, phosphorus, and potassium (NPK) (e.g., 50, 60, and 400 mg kg−1) minimized the life cycle of nanofertilized wheat plants compared with those fertilized with regular nutrients contained in the form of polymers (chitosan). Wheat (Triticum aestivum) plants fertilized with chitosan NPs containing NPK via foliar application had a shortened harvesting duration (130 days) after planting compared with 170 days after planting if normal fertilizers containing NPK were used.
Several scientists described the benefits of engineered nanomaterial formulations with pesticide properties17,18. The study conducted by Chhipa18 showed that the pesticide properties of silver NPs within major components presented a noticeable influence against numerous fungal species. In contrast, when Cu NPs were utilized, the efficiencies of the applications against bacteria and fungi were remarkably improved. Other several materials such as hezaconazole and nanosulfur also presented high efficiencies as fungicides. The only constraints when using such nanomaterials as pesticides are their ecological impacts, which are not well understood yet18. Adisa et al.17 studied polymer-support nanopesticides such as nanogels, nanospheres, nanofibers, and nanocapsules classified as antimicrobials materials that possess different environmental persistence abilities. Generally, nanospheres can store active components dispersed throughout nanomatrices; however, their active ingredients are encased in the polymeric matrix17.
On another note, the water problem has recently become a global issue, and water reuse could be one of the means of reducing the strain on already depleting water resources19. The reported causes of domesticated water reprocessing were established to be osculated from one region to another (e.g., 32% in Asia and 51% in northern Europe for environmental purposes; 46% in California for agriculture; 7% in Japan for agriculture; 44% in Florida, 25% in Tunisia, and 4% in Australia for total consumption; 25% in Spain for agriculture; and 75% in Israel for agriculture. Moreover, generally 500 Mm3 year−1 wastewater used in Mexico and China were directly reused without treatment20,21,22. Consequently, inorganic contaminants may accumulate in irrigation water or soils. Thus, the novelty in this work is to synthesize ZnO, MgO and SiO2 NPs using a low-cost and safe method. Also, it studied the effects of these NPs on the quality of irrigation water, the contents of some heavy metals in soils and plants, and the productivity of Origanum majorana (marjoram).
Material and methods
Materials
Lemon (Citrus limon)23 peel extracts were used for the green synthesis of MgO, SiO2, and ZnO NPs. The magnesium nitrate, zinc sulfate, and sodium metasilicate possessed high purity (≥ 98%). All materials were purchased from Merck Chemicals Ltd., whereas the fresh peels of lemons were collected from different lemon farms in Egypt. The fresh peels were first washed with distilled water and then soaked in an ethanol (C2H5OH) and ammonium hydroxide (NH4OH) solution purchased from Merck Chemicals Ltd., Darmstadt, Germany.
Preparation of MgO, SiO2, and ZnO NPs
MgO, SiO2, and ZnO NPs were prepared in two main steps: (1) the collection of lemon peel extract and (2) the synthesis of MgO, SiO2, and ZnO NPs.
Preparation of lemon peel extract
The lemon peels were washed with distilled water several times to remove any dust and then dried at 60 °C inside a furnace for 48 h. The dried lemon peels were ground, crushed, and sieved into a suitable size. The extract was then obtained at a concentration of 250 g L−1 at 25 °C for 24 h with steady shaking. Thereafter, the extract was filtered using a filter paper.
Synthesis of MgO, SiO2, and ZnO NPs
For preparing MgO, SiO2, and ZnO NPs, we added 0.5 mol L−1 of magnesium nitrate, sodium metasilicate, and zinc sulfate aqueous solution to the lemon peel that was separated previously from the extraction solution. The solution was then boiled to 70 °C for 1 h until it was reduced into a white-colored solution. This color change is considered a mark of the formation of soluble fractions from the peel extract. It was demonstrated that the ethanol lemon peel extract contained hesperidin flavanol, which discharges aglycone that may be used as a reducing agent24,25. The pH of each NP mixture was adjusted through the addition of ammonium hydroxide solution (0.1 mol L−1 to maintain the pH values of 9.7, 11.58, and 6.95 for MgO, SiO2, and ZnO NPs, respectively. Afterward, the precipitates were washed several times with deionized water, centrifuged and collected in a clayey crucible, and heated in a muffle at 500 °C for 3 h for both MgO and ZnO NPs and at 700 °C for SiO2 NPs. Elevating the temperature in the muffle was mandatory to remove any organic residuals. Finally, a white precipitate for each NP was obtained and packed carefully for further characterization. The probable mechanisms for the production of MgO, ZnO, and SiO2 NPs are defined below:
Characterization of the prepared nanoparticles
The MgO, SiO2, and ZnO NPs were characterized using the following procedures. Powdered NPs were analyzed using X-ray diffraction (XRD) (PAN Analytical X'Pert TopScore Plus Diffractometer) operated at 40 kV with a current of 30 mA under Cu-Kα radiation of a 2θ range of 10°–80°. The surface morphologies of the NPs were observed using transmission electron microscopy (TEM) with an elevated-resolution (JEOL JEM-1400 UHR, operated at 80 kV). The chemical structures of the prepared NPs were investigated using Fourier transform infrared spectroscopy (FTIR) infrared spectra (using a Nicolet Avatar 230 spectrometer. UV–Vis spectrophotometer between 200 and 800 nm wavelength range (Elico EI 301E, India) was used for scanning different prepared nanoparticles.
Soil sampling and analysis
Soil samples were collected from a constant depth of 0–30 cm from the El-Gabal El-Asfar area, Egypt. Some soil and water properties are listed in Table 1. The soil samples were air-dried, crushed, and sieved through a 2-mm sieve to ensure the removal of gravel and organic waste. The soil texture was determined following the international pipette method. The other properties of the soil samples, including organic matter content, pH, and electrical conductivity, were determined according to published literature25,26,27. The heavy metal contents were determined using inductively coupled argon plasma optical emission spectrometry (ICAP 6500 Duo, Thermo Scientific, England). N, P, and K were determined in an acid digested solution, which was prepared according to Dahnke and Johnson28. The available nitrogen in the soil samples was extracted using a 2M potassium chloride solution and determined according to29. The available potassium and phosphorous were extracted using a DTPA+ ammonium bicarbonate solution and measured following the method described by Soltanpour30.
Adsorption experiments
Series of experiments was conducted to investigate the effects of different pH levels on the removal of Cu2+and Fe3+ ions using MgO, SiO2, and ZnO NPs as adsorbent materials with an initial concentration of 50 mg L−1 for both Cu2+ and Fe3+. The solid to liquid ratio was 10 g L−1 the shaking rate was 175 rpm, and the temperature was adjusted to 25 °C. Solutions with different pH values were prepared, and the pH was adjusted by adding nitric acid (0.1 M mol). After the prevailing 24 h of adsorption, the concentrations of the remaining Cu2+ and Fe3+ ions in each solution were detected using inductively coupled argon plasma optical emission spectrometry (ICAP 6500 Duo, Thermo Scientific, England).
The adsorption isotherm of Cu2+ and Fe3+ was obtained using the prepared NPs as adsorbents, in which a series of concentrations of Cu2+ and Fe3+ was prepared by dissolving copper sulfate and iron chloride with an initial concentration of copper and iron ranging from 20 to 500 mg L−1. The initial pH values for the Cu2+ and Fe3+ solutions were 5.2 and 3.2, respectively. Generally, 50 ml of each solution and 0.5 g of the adsorbent were mixed in a 100-ml sealed conical flask shaken at a constant speed of 175 rpm in a thermostatic water bath at 25 °C. After 24 h of adsorption, the concentrations of the remaining Cu2+ and Fe3+ in each solution were determined.
Pot experiments
Pot experiment was carried out in green house of Desert Research Center, Egypt. located at 30° 7.29′ N, 31° 18.93′ E. Pot experiments were conducted during the cropping season of 2020–2021 to investigate the effects of MgO, SiO2, and ZnO NPs on plant yield and the availability of some heavy metals in both the soil and marjoram hat were polluted at three levels with either Fe3+ or Cu2+. Marjoram was planted in pots containing 18 kg of soil after approximately 30 days from seed germination. Fertilizer doses were added to all treatments (as ammonium sulfate, calcium superphosphate, potassium sulfate, and biofertilizers)31. The experimental design was factorial with three replicates at three levels (0, 5, and 10 mg kg−1) of each pollutant (Cu2+ and Fe3+) and at 0, 150, and 300 mg kg−1 of each of the MgO, SiO2, and ZnO NPs. A sum of 35 treatments was performed after 30 and 60 days from the transplanting date (April 21 and May 23). The plants were irrigated twice a month with 55 cm3 for each treatment. After 97 days from the planting, the marjoram plants were cut at the soil surface and washed with deionized water. The plants were oven-dried at 70 °C for 48 h, weighed for dry matter yield, and ground. The plants and soil samples of the different treatments were digested using H2SO4–H2O232. The heavy metal contents were detected using ICAP.
Statistical analysis
The data obtained in the present work were statistically analyzed, and the differences between the means of the different treatments were considered significant when they were greater than the values of the least significant difference at the 5% level using the Statistic program version No. 9. Alltreatments were used in a factorial design.
Statement
The collection of lemon peel and the cultivated Origanum majorana samples was done by getting the permission from the local suppliers. Te authors confirm that all methods were performed in accordance with the relevant guidelines and regulations.
Results and discussion
Characterizations of the NPs
XRD is a widely used method for determining particle size and NP structure. The XRD of the different NPs produced with the lemon peel extract is shown in Fig. 1. The following is how the Debye–Scherrer equation was used to determine the dimensions of the MgO, SiO2, and ZnO NPs:
The X-ray diffraction profile of NPs synthesized using the lemon peel extract.
where D is the crystal volume, λ is the wavelength of the X-ray radiation (λ = 0.15406 nm) for Cu-Kα,K is frequently taken as 0.9, and β is the line width at half-maximum height. The peaks of the MgO NPs matched with the plane (JCPDS card No. 89–7102) and were found at 2θ = 36.72° (111), 2θ = 42.80° (200), 2θ = 62.38° (202), 2θ = 74.5° (311), 2θ = 78.5° (312), (222). The MgO NPs produced with lemon peel extract had a crystallized face-centered cubic (fcc) phase of magnesium oxide, according to the XRD spectrum33. Using Scherrer's formula, the crystal size was predicted to be around 16.77 nm. The SiO2 NPs had peaks that correspond to the planes 2θ = 28.4° (040), 2θ = 31.5° (200), 2θ = 36.06° (130), 2θ = 48.4° (330), and 2θ = 56.9° (330)34. The XRD spectra indicate that the SiO2 NPs made from the lemon peels were crystalline. Using Scherrer's formula, the calculated crystal diameters were around 42.6 nm. In addition, the ZnO NP patterns also suggest that the planes were approximately 2θ = 31.8° (100), 2θ = 34.4° (100), (002), 2θ = 36.3° (101), 2θ = 47.5° (102), 2θ = 56.6° (110), 2θ = 56.69° (110), 2θ = 62.8° (103), 2θ = 67.98° (200), and 2θ = 69.1° (200), (201). These findings are in line with those of other researchers who have shown ZnO diffractograms16,35. As indicated in Fig. 1, no contaminant diffraction peaks were identified. These findings revealed that the produced ZnO was extremely pure. No usual graphitic carbon diffraction peaks were found. Because graphitic carbon is naturally amorphous, its existence cannot be ruled out. The sample's highly crystalline nature is indicated by the crisp and high diffraction peaks36. High heat treatment is likely to provide sufficient kinetic energy for rearranging atomic groupings and hence the development of NP crystal structures37. ZnO was synthesized in this process at a sufficiently high temperature of around 500 °C, resulting in a product with a crystalline structure. Using Scherrer's formula, the crystallite size of the ZnO nanocrystallite was around 60.5 nm.
TEM images provide a more detailed insight into the interior structure of NPs. Figure 2 shows a TEM image of the MgO, SiO2, and ZnO NPs produced with lemon peel extract. The circular structures are built of unique individuals of the distinct manufactured NPs, according to the increased two-dimensional picture of the NPs. Each produced NP has a size of about less than 100 nm, as measured by the TEM imaging. This size corresponds to that calculated from the XRD pattern. The FTIR technique was used to determine the probable chemical bonds in the lemon peel extract and the produced NPs. The FTIR spectra of the MgO, SiO2, and ZnO NPs, as well as that of the lemon peel extract, are shown in Fig. 3. The spectrum of the lemon peel extract had a strong peak at around 3200–3700 cm−1, which may be attributed to the stretching mode of the hydroxyl of the phenols, which also coincide with the N–H of the amines, which could be attributable to the various bioactive chemicals found in lemon38,39. The symmetrical and asymmetrical C–H of the aliphatic groups has been assigned to two minor intensity peaks at about 2925 cm−1. The bending vibration of the OH group was attributed to a wide broad peak at about 1717 cm−1, which could be due to chemisorbed and/or physisorbed moisture on the surface of the NPs40. The occurrence of C–O symmetric stretching of alcohol and vibrating C–H of the –CH=CH of the ethylene structure can be seen in the bands at 1019 and 616 cm−1, respectively. When these peaks are compared with the spectra of the MgO NPs, a decrease in the peak position of the MgO NPs is observed. The MgO NPs had an absorption band at 450–850 cm−1 in the FTIR spectrum. The O–H stretch manifested as a very broad band in the spectra, spanning 3700 cm−141,42. The saturated main peak between 1092 and 1456 cm−1 indicate significant concentrations of carbon and are also characteristic of the ligand40. Glycone steroids may have played a key role in the stabilization and capping of MgO NPs in our research25,38,39. When these peaks are compared with the spectra of the ZnO NPs, the peak broadening of the ZnO NPs is reduced. The typical Zn–O stretching vibration of the ZnO NPs caused a significant peak at about 450 cm−143,44. Before the calcination of the intermediate product to ZnO NPs, biomolecules were responsible for the conversion of ZnSO4 to Zn(OH)2.
The TEM micrograph of MgO, SiO2, and ZnO nanoparticles synthesized by lemon peel extract.
The FTIR spectra of the MgO, SiO2, and ZnO nanoparticles and lemon peel extract.
Figure 3 shows the FTIR spectra of the produced SiO2NPs. Si–O has a band at around 790 cm−1, and the symmetric stretching and bending vibrations of Si–O–Si have bands at around 477 and 619 cm−1, respectively44. Bending vibration occurs when oxygen moves at a perfect angle to the Si–Si bands in the Si–O–Si plane45,46. The stretching vibration of the Si–O–Si band, wherein the bridging oxygen atom shifts parallel to the Si–Si lines in the reverse direction of their Si neighbors, corresponds to the band at approximately 1072 cm−1. The 3555-cm−1 band is specific to Si–OH hydrogen-bonded stretching modes46. The UV–visible spectra of lemon peel extract, as well as MgO, SiO2, and ZnO NPs are shown in Fig. 4. The qualitative UV‐VIS profile of ethanolic extract of lemon peel was taken at the wavelength of 300 nm to 500 nm owing to the sharpness of the peaks and proper baseline. The profile showed the peaks at 242, 246, 254, 258, 262, 266, 270, 274, 278, 282, 286, 290, 294, 298, 302, 306, 310, 314, 318, 322, 326, 330, 334, 338, 342, 346, 352 and 354 nm. In the UV–VIS spectra the presence of more peaks in the wavelength region from 200 to 500 nm is obvious and indicates the existence of unsaturated groups and heteroatoms compounds containing S, N, O47. The peaks at 354 nm indicate the presence of organic chromophores within the lemon peel extract. The peak located between 320 and 360 nm should be ascribable to the existence of phenolic mixtures1. Similarly, the band between 280 and 315 nm signposts to the presence of flavonoids and aloin1. Nevertheless, Jain et al.47, stated that, the use of UV–visible spectrophotometery in the studding of complex extract is limited by the essential difficulties in assigning the absorption peaks to any certain components in the structure. Hence, UV–VIS outcomes must be accompanied with GC/MS, to assist appropriate extract characterization and component identification47. The UV–visible spectra of MgO NPs are shown in Fig. 4. The absorption spectra of the reaction media with absorbance at 300 nm established the existence of MgO NPs. This verifies the reduction of Mg (NO3)2 and the emergence of MgO48. The absorption spectra of the green synthesized ZnO NPs exhibited maximum optical absorption band at 358 nm1. The green synthesized SiO2 nanoparticles exhibited one absorption peak at 208 nm, attributable to the characteristic absorption of SiO249.
UV–Vis spectrophotometer of lemon peel extract and different prepared NPs.
Batch adsorption experiments
Effects of the initial pH on the adsorption efficiency
The pH of any solution is considered one of its most important parameters that basically influence the adsorption of ions such as Cu2+ and Fe3+, as studied in this work. To evaluate the effects of pH on the removal efficiency of Cu2+ and Fe3+, experiments were performed in pH ranging from1 to 5 and 1 to 3.5, respectively. The initial concentrations of either Cu2+ or Fe3+ were close to 100 mg L−1, as shown in Fig. 5. The pH values exceeding 5 and less than 3.5 for Cu2+ and Fe3+ ions, respectively, were not studied to avoid the natural phenomenon of Cu2+ and Fe3+ precipitation in hydroxide forms. Apparently, the variations in the removal percentages with different pH values were approximately constant, and maximum values were obtained within pH values ranging from 3 to 5 for Cu2+, where removal percentages of 89.9%, 83.3%, and 68.36% were achieved for ZnO, MgO, and SiO2 NPs, respectively. Comparatively, the removal percentages were 82%, 80%, and 65% for the adsorption of Fe on the ZnO, MgO, and SiO2 NPs, respectively, at pH 3.3.
Effect of pH on adsorption of Cu2+ (a) and Fe3+ (b) ions (conditions: 10 gl−1 adsorbent, 10 ml of 50 mg L−1 of ions, duration of oscillation time of 24 h at temperature 25 °C).
In general, adsorption percentages are reduced with lower pH levels. This is may be because of the reduced number of negative sites and the competition between the positive copper, iron, and hydrogen ions on these negative adsorption sites50. By increasing the pH of media, more adsorptive sites are created, and the adsorption capacity is increased. However, with continued increases in pH values, the formation of precipitates of Cu2+ and Fe3+ hydroxide is increased. Accordingly, adsorption experiments at pH values of 5.2 and 3.3 were preferable for Cu2+ and Fe3+, respectively.
Adsorption isotherm models
Adsorption isotherms were used to easily describe the adsorption of different fractions of sorbet molecules that are partitioned between liquid and solid phases at equilibrium. Generally, the adsorption of Cu2+ and Fe3+ ions on the ZnO, MgO, and SiO2 NPs was modeled using two adsorption isotherms.
Freundlich isotherm
The Freundlich isotherm is a model used to represent monolayer (chemisorption) and multilayer (physisorption) adsorption. It is founded on the supposition that molecules adsorb onto the uneven surface of an adsorbent51. Freundlich's equation is written in linear form as follows:
The Freundlich isotherm coefficients KF and n are calculated first from the intercept and slope of a chart of logqe vs. logCe, as shown in Fig. 6. In this investigation, n values greater than unity were discovered, indicating chemisorptions (Table 2)52. L-type isotherms with n > 1 suggest a high affinity between the adsorbate and the adsorbent and are suggestive of chemisorption53. With increasing temperature, the Freundlich constant (KF) shows that the adsorption mechanism is endothermic.
Linearized Freundlich isotherms for Cu2+ and Fe3+ ions adsorption on ZnO, MgO, and SiO2 NPs at different temperatures.
Langmuir isotherm
The Langmuir isotherm assumes the adsorption of a monolayer on a uniform surface with a finite number of adsorption sites. Once a site is filled, no further sorption can take place at that site as the surface will eventually reach a saturation point where the maximum adsorption of the surface will be achieved. The linear form of the Langmuir isotherm model is described as follows:
where KL is the Langmuir constant related to the energy of adsorption, and qmax is the maximum adsorption capacity (mg g−1)54. The slope and intercept of plots of Ce/qe versus Ce at different temperatures were used to calculate qmax and KL, as is shown in Fig. 7. The Langmuir isotherm parameter was appropriate for Cu2+ and Fe3+ adsorption on the ZnO, MgO, and SiO2 NPs and yielded isotherms that were in good agreement with the observed behaviors, as presented in Table 3. The Cu2+and Fe3+ adsorption capacities on the ZnO, MgO, and SiO2 NPs at room temperature (297 K) were respectively 135, 66, and 58 mg g−1 for Cu2+ and 104, 100, and 94 mg g−1 for Fe3+, as shown in Table 3. These are much higher than the adsorption capacities of other adsorbents reported in other relevant literature:that of activated carbon reached 3.37 mg g−155, whereas the adsorption of hematite reached 4.94 mg g−156.
Linearized Langmuir isotherms for Cu and Fe ions adsorption on ZnO, MgO, and SiO2 NPs at different temperatures.
Effects of ZnO, MgO, and SiO2 NPs and polluted irrigated water containing Cu2+ and Fe3+ on the soil and plants
Effects of ZnO, MgO, and SiO2 NPs and polluted irrigated water containing Cu2+ on the available concentrations of Cu2+ in the soil and plants
The data listed in Table 4 show the effects of adding Cu2+at concentrations of 5 and 10 mg kg−1 together with different treatments of NPs. It can be clearly seen that the NP application without the addition of any pollutant reduced the available Cu2+ in the studied soil samples. The order of the effects of the NP application was as follows: Zn2 > Zn1 > Mg2 > Si2 > Mg 1 > Si1 > C (control). The highest values of the available Cu2+ were observed in the control treatment, whereas the lowest values were obtained when Zn2 was added57.
There was a significant difference between all treatments except for Si2/Mg2 and Si1/Mg1. When Cu2+ was added to the soil as an external pollutant to increase the original exit values by 5 mg kg−1, the effects of the NP application on the availability of Cu2+ extracted using DTPA took the following order: Zn2 > Zn1 > Si2 > Mg2 > Si1 > Mg1 > C (control). The highest value of the effects of NP addition on artificially polluted soils with Cu2+ (5 mg kg−1) was found when Zn2 was added to the soil, whereas the lowest effect was found when Mg1 was added58. There was a significant difference between all treatments except for Si2/Mg2 and Si1/Mg1, similar to what was observed in the control experiments. Increasing the original values of Cu2+ by 10 mg kg−1 changed the order of effects of the NPs to the following: Zn2 > Zn1 > Mg2 > Si2 > Mg1 > Si1 > C (control).
There was a significant difference between all treatments except for Si2 and Mg1. It can beclearly seen that the highest reduction effect on the available Cu2+ in the three trials studied (thecontrol, 5 mg kg−1, and 10 mg kg−1) was related to the addition of Zn2. The mean values for the three NPs presented significant differences except for Si1 and Mg1. The data presented in Table 4 explore the effects of NPs on Cu2+ uptake through plants that were osculated among the higher and lower values compared with the control experiments. The order for increasing Cu2+ uptake through plants without the addition of Cu2+ was as follows:Si1 > Zn2 > Si2 > Zn1 > Mg1 > C (control) > Mg2.
There was a significant difference between all treatments except for Si2/Zn2 and C(control)/Mg1. When Cu2+ was added to the soil at a constant concentration of 5 mg kg−1, the order of effects of the NP application was as follows: C (control) > Si1 > Si2 > Mg1 > Zn1 > Zn2 > Mg2. This indicates that the addition of NPs to the soil system decreased Cu2+ uptake through plants.
There was a significant difference between all treatments except for Zn1, Si2, and Mg1. Increasing the addition of Cu2+ pollutants to the soil to 10 mg kg−1 changed the sequence of effects of NP addition to the following order: C (control) > Mg1 > Mg2 > Zn2 > Si1 > Zn1 > Si2. There was a significant difference between all treatments except for Zn1 and Mg2. The application of NPs minimized the Cu2+ levels in marjoram because of the antagonistic impacts of metals. The trend of these results agrees with those reported by Saifullah et al.59, Hussain et al.60, and Wang et al.61.
Effects of ZnO, MgO, and SiO2 NPs and polluted irrigated water containing Fe3+ on the available concentrations of Fe3+ in soil and plant
The effects of adding Fe at concentrations of 5 and 10 mg kg−1 with different NP treatments are listed in Table 4. It can be clearly seen that the NP application without the addition of any pollutants reduced the available Fe3+ in the soil samples. The order of the effects of the NP application on the reduction of available Fe was found as follows: Zn2 > Zn1 > Mg2 > Mg1 > Si1 > Si2 > C (control)57. The highest values of the available Fe3+ were observed in the control, whereas the lowest values were obtained when Zn2 was added.
There was a significant difference between all treatments except for Si1 and Mg1. When Fe3+ was added to the soil as an external pollutant source to increase the original exit values by 5 mg kg−1, the effects of the NPs addition on the availability of Fe3+ extracted using DTPA took the following order: Zn2 > Zn1 > Si2 > Mg2 > Si1 > Mg1 > C (control).This is considered similar to what was observed with the same treatment of Cu2+. The highest values were found when Zn2 was added to the soil, whereas the lowest values were found when Mg1 was added. There was a significant difference between all treatments except for Mg1 and the control. Increasing the concentration values of Fe3+ to 10 mg kg−1changed the order of the effects of NP addition to the following: Zn2 > Zn1 > Si2 > Mg2 > Si1 > Mg1 > C (control).
There was a significant difference between all treatments. Clearly, the highest effect in the three trials studied in this work (control, 5 mg kg−1, and 10 mg kg−1) was related to the addition of Zn258,62. The data presented in Table 4 also explore the effects of NPs on Fe3+ uptake through plants that were osculated among the higher and lower values compared with the control experiments. The order of the effects of NP addition on increasing Fe3+ uptake through plants was as follows: Si2 > Mg2 > C (control) > Si1 > Mg2 > Zn1 > Zn2.
There was a significant difference between all treatments except for the control and Si1. When Fe3+ was added to the soil at a constant concentration of 5 mg kg−1, the order of the effects of NP application was as follows: C (control) > Si1 > Mg1 > Zn2 > Mg2 > Zn1 > Si2.Thisindicates that the addition of NPs to the soil system had positive effects on the Cu2+ uptake through plants.
There was a significant difference between all treatments except for Mg2 and Zn1. Increasing the addition of Fe3+pollutants to the soil to 10 mg kg−1 changed the sequence of the effects of NP addition on increasing Fe3+ concentrations inside the plant tissue to the following order: C (control) > Si1 > Zn1 > Mg1 > Mg2 > Zn2 > Si258,62.
There was a significant difference between all treatments. At the root surface, NPs can compete with Fe3+ as these metals are being transported by common transporters in the roots63. Higher Zn concentrations in the roots may inhibit Fe3+ uptake by marjoram plants. The trend of these results agrees with those reported by Ali et al.60, who suggested that the improved Zn nutritional status with foliar-applied ZnO NPs may suppress the expression of Zn2+ transporters in roots, decreasing the Cd2+ accumulation by roots. This variation in metal accumulation by plants under NP treatments might be due to the variation in the sizes and shapes of NPs as well as the crop species and NP application modes.
Effect of Cu2+ and Fe3+ additives and ZnO, MgO, and SiO2 NPs treatment on the availability of N, P, and K in soils
Effect of Cu2+ additives and ZnO, MgO, and SiO2 NPs treatment on the availability of N, P, and K in soils
The effects of Cu2+ additives with two concentrations of 5 mg kg−1 and 10 mg kg−1 simultaneously with different treatment of NPs are listed in Table 5. It was clearly seen that the effects of NPs application on the availability of substantial concentrations of N without any pollutants additives resulted in an osculating in the reduction or increment of the available N in the soil system. The order of sequence for the effects of NPs application on reducing available N was found to take the following sequence Mg2 > Mg1 > C (control) > Si2 > Zn2 > Zn1 > Si1. he highest values that were affected the reduction of the available N were observed with Mg2, whereas the lowest values were obtained when Si1 was added. There was a significant difference between all treatments except for the treatments of (control and Mg1)58,62. When Cu2+ was added to the soil as an external pollutant to increase the original exit values by 5 mg kg−1, the effects of NPs application on the availability of N were found to take the following order Mg2 > Zn2 > Si2 > Si1 > Mg2 > Si2 > C (control) > Zn1. The highest value of the effects of adding NPs on the artificially polluted soils with Cu2+ (5 mg kg−1) to reduce the availability of N was found when Mg2 was added to the soil, whereas the lowest effect was found when Zn1 was added. There was a significant difference between all treatments except for the treatments of (control and Si2) and (Z2 and Si1). Increasing the values of polluted Cu2+ to 10 mg kg−1 resulted in changing the order of effects of NPs on the availability of N to the following order Si2 > Mg1 = Mg2 = Si1 = Zn2 > C (control) > Zn1. There was a significant difference between all treatments except for the following treatments Mg1, Mg2, Si1, and Zn2. It was clearly seen that the highest effects in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 were osculated among Mg2 and Si2. The effects of Cu2+ additives as two concentrations of 5 mg kg−1 and 10 mg kg−1 simultaneously with different treatment of NPs on available phosphorous (P) are listed in Table 5. It was clearly seen that the effect of NPs application on the availability of substantial concentrations of P without any pollutants additives resulted in an osculating of the reduction or increment of the available P in the soil system. The order of sequence for the effects of NPs application on reducing available P was found to take the following sequence Zn2 > C (control) > Mg2 > Mg1 > Zn1 > Si1 > Si2. The highest values that affected the reduction of the available P were observed with Zn2, whereas the lowest values were obtained when Si2 was added. There was a significant difference between all treatments except for the treatments of (control and Zn2). When Cu2+ was added to the soil as an external pollutant to increase the original exit values by 5 mg kg−1, the effects of NPs application on reducing the availability of P was found to take the following order Mg2 > Si2 > Mg1 > Zn1 > C (control) > Si1 > Zn245,62. The highest value of the effects of adding NPs on the artificially polluted soils with Cu2+ (5 mg kg−1) to reduce the availability of P was found when Mg2 was added to the soil, whereas the lowest effect was found when Zn2 was added. There was a significant difference between all treatments except for the treatments of (Si2 and Mg2). Increasing the values of an external pollution of Cu2+ to 10 mg kg−1 resulted in changing the order of effects of NPs on the availability of P to the following order C (control) > Zn1 > Mg2 > Si1 = Si2 > Mg1 > Zn2. There was a significant difference between all treatments except for the following treatments (Si1 and Si2). It was clearly seen that the highest effects in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 were osculated among Zn2, Mg2, and control. The effects of Cu2+ additives with two concentrations of 5 mg kg−1 and 10 mg kg−1 simultaneously with different treatment of NPs on the availability of K are also listed in Table 5. It was clearly seen that the effect of NPs application on the availability of substantial concentrations of K without any pollutants additives resulted in an osculation in the reduction or increment of the available concentrations of available K in the soil system. The order of sequence for the effects of NPs application on reducing the available concentrations of K was found to take the following sequence Mg2 > Si2 > Mg1 > C (control) > Si1 > Zn1 > Zn2. The highest values affected the reduction of the available K were observed with Mg2, whereas the lowest value was obtained when Zn2 was added. There was a significant difference between all treatments except for the treatments of (Si2 and Mg1). When Cu2+ was added to the soil as an external pollutant to increase the original exit values by 5 mg kg−1, the effects of NPs application on the availability of K were found to take the following order Si1 > Mg1 > Zn2 > C (control) > Mg2 > Zn1 > Si2. The highest value of the effect of adding NPs on the artificially polluted soils with Cu2+ (5 mg kg−1) to reduce the availability of K was found when Si1 was added to the soil, whereas the lowest effect was found when Si2 was added. Generally, there was a significant difference between all treatments. Increasing the values of an external polluted Cu2+ to 10 mg kg−1 resulted in changing the order of effects of NPs on the availability of K to the following order Si2 > Si1 > Mg2 > Zn2 > Mg1 = Zn1 > C (control). There was a significant difference between all treatments. It was clearly seen that the highest effects in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 on K availability were osculated among Mg2, Si1, and Si2. On the other hand, the lowest effects were attributed to the Zn2 in the control experiment, whereas in the experiments that have been carried out with the addition of Cu2+ (5 mg kg−1 and 10 mg kg−1), the effects of Si2 and control were more dominant. The highest values of available K were found with the control experiment followed by the experiments that were carried out with the addition of an external Cu2+ with concentrations of 5 mg kg−1 and 10 mg kg−1, respectively.
Effect of Fe3+ additives and ZnO, MgO, and SiO2 NPs treatment on the availability of N, P, and K in the treated soils
The effects of Fe additives with two concentrations of 5 mg kg−1 and 10 mg kg−1 simultaneously with different treatment of NPs are listed in Table 6. It was clearly seen that the effect of NPs application on the availability of substantial concentrations of N without any an external Fe additives resulted in an osculating in the reduction or increment of the available N in the soil system. The order of sequence for the effects of NPs application on reducing the available N was found to take the following sequence C (control) = Mg1 > Si1 > Mg2 > Zn2 > Zn1 > Si1. The highest values that affected the reduction of the available N were observed with both control and Mg1, whereas the lowest values were obtained when Si1 was added. There was a significant difference between all treatments except for the treatments of (control and Mg1). When Fe was added to the soil as an external pollutant to increase the original exit values by 5 mg kg−1, the effects of NPs application on the reduction of available N were found to take the following order Zn2 > Si2 > Mg2 = C (control) > Si1 = Mg1 > Zn1. The highest value of the effects of adding NPs on the artificially polluted soils with Fe3+ (5 mg kg−1) to reduce the availability of N was found when Zn2 was added to the soil, whereas the lowest effect was found when Zn1 was added. There was a significant difference between all treatments except for the treatments of (control, Si1, Mg1, and Mg2)58,62. Increasing the values of an external addition of Fe3+ to 10 mg kg−1 resulted in changing the order of effects of NPs on reducing the availability of N to the following order Si1 > Zn1 = Si2 = Zn2 > C (control) > Mg1 > Mg2. There was a significant difference between all treatments except for the following treatments (control and Zn2), (Zn2 and Mg1), and (Zn1 and Si12). It was clearly seen that the highest effect in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 was osculated among Mg1, control, Zn2, and Si1. On the other hand, the lowest effects were attributed to the Si1 in the control experiment, whereas in the experiments that have been carried out with the addition of Fe3+ with concentrations of 5 mg kg−1 10 mg kg−1, the effects of Zn1 and Mg2 were more dominant. The highest values of available N were found with the control experiment followed by experiments that were carried out with the addition of Fe3+ at concentrations of 5 mg kg−1 and 10 mg kg−1. The effects of Fe3+ additives with two concentrations of 5 mg kg−1 and 10 mg kg−1 with different treatment of NPs on the reduction of available P are listed in Table 6. It was clearly seen that the effect of NPs application on the availability of substantial concentrations of P in soil without any pollutants additives resulted in an osculating in the reduction or increment values of the available P in the soil system. The order of sequence for the effects of NPs application on reducing the available P was found to take the following sequence Zn2 > C (control) > Mg2 > Mg1 > Zn1 > Si1 > Si2. The highest values affected the reduction of the available P were observed with Zn2, whereas the lowest values were obtained when Si2 was added. There was a significant difference between all treatments62. When Fe3+ was added to the soil as an external pollutant to increase the original exit values by 5 mg kg−1, the effects of NPs application on the availability of P were found to take the following order Mg2 > Si2 > Mg1 > Si2 > Zn2 > Zn1 > C (control). The highest value of the effects of adding NPs on the artificially polluted soils with Fe3+ (5 mg kg−1) to reduce the availability of P was found when Mg2 was added to the soil, whereas the lowest effect was found when Zn1 was added. There was a significant difference between all treatments except for the treatments of (Si1 and Mg2). Increasing the values of an external addition of Fe3+ to 10 mg kg−1 resulted in changing the order of effects of NPs on the availability of P to the following order Si1 > Mg1 > Mg2 > Si2 > Zn2 > Zn1 > C (control). There was a significant difference between all treatments except for the following treatments (Zn1, Zn2, Si2, and Mg2).
It was clearly seen that the highest effect in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 was osculated among Zn2, Mg2, and Si1. The effects of Fe3+ additives with two concentrations of 5 mg kg−1 and 10 mg kg−1 simultaneously with different treatment of NPs on the reduction of available K are listed in Table 6. It was clearly seen that the effect of NPs application on the availability of substantial concentrations of K in soil without any pollutants additives resulted in an osculating in the reduction or increment of the available concentrations of K in the soil system. The order of sequence for the effects of NPs application on reducing the available concentrations of K was found to take the following sequence Mg2 > Si2 > Mg1 > C (control) > Zn1 > Si1 > Zn2. The highest values affected the reduction of available K were observed with Mg2, whereas the lowest values were obtained when Zn2 was added58,62. There was a significant difference between all treatments. When Fe3+ was added to the soil as an external pollutant to increase the original exit values by 5 mg kg−1, the effects of NPs application on the availability of K was found to take the following order Zn2 > Si2 > C (control) > Mg2 > Zn1 > Mg1 > Si1. The highest value of the effects of adding NPs on the artificially polluted soils with Fe3+ (5 mg kg−1) to reduce the availability of K was found when Zn2 was added to the soil, whereas the lowest effect was found when Si1 was added. There was a significant difference between all treatments except for (Mg1 and Mg2). Increasing the values of an external addition of Fe3+ to 10 mg kg−1 resulted in changing the order of effects of NPs on the availability of K to the following order C (control) > Zn2 > Mg2 > Zn1 > Mg1 > Si2 > Si1. There was a significant difference between all treatments except for (Z1 and Mg1)62. It was clearly seen that the highest effects in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 on K availability were osculated among Mg2, Zn2, and control.
Effect of Cu2+ and Fe3+ additives and ZnO, MgO, and SiO2 NPs treatment on the accumulation of N, P, and K in the plant
Effect of Cu2+ additives and ZnO, MgO, and SiO2 NPs treatment on the accumulation of N, P, and K in the plant
The effects of Cu2+ additives with two concentrations of 5 mg kg−1 and 10 mg kg−1 simultaneously with different treatment of NPs on increasing the total amounts of N in the plant are listed in Table 6. It was clearly seen that the effect of NPs application on increasing the total concentrations of N without any Cu2+ additives resulted in an osculation in the reduction or increment of N in the plant62. The order of sequence for the effects of NPs application on the increasing the total N was found to take the following sequence Mg2 > Zn2 > Si2 > Si1 > C (control) > Zn2 > Zn1 > Si1. The highest values affected the increases of the available N in the plant were observed with Mg2, whereas the lowest values were obtained when Si1 was added. There was a significant difference between all treatments except for the treatments of (control and Si2) and (Si1 and Mg1). When Cu2+ was added to the soil as an external pollutant to increase the original exit values by 5 mg kg−1, the effects of NPs application on the increment of total N were found to take the following order Si2 > C (control) > Mg1 > Zn1 = Mg2 > Zn2 > Si1. The highest value of the effects of adding NPs on the artificially polluted soils with Cu2+ (5 mg kg−1) to increase the total concentrations of N in the plant was found when Si2 was added to the soil, whereas the lowest effect was found when Si1 was added62. There was a significant difference between all treatments except for the treatments of (control and Si2) and (Z1 and Mg2). Increasing the values of an external addition of Cu2 + to 10 mg kg−1 resulted in changing the order of effects of NPs on increase the total concentrations of N in the plant to the following order Si2 > Si1 > C (control) > Zn2 = Mg1 > Zn1 > Mg2. There was a significant difference between all treatments except for the following treatments (control and Si1) and (Zn1, Zn2, and Mg1). It was clearly seen that the highest effects in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 were osculated among Mg2, Si2, and Si2, respectively. The effects of Cu2+ additives with two concentrations of 5 mg kg−1 and 10 mg kg−1 simultaneously with different treatment of NPs on increasing the total amounts of P in the plant are listed in Table 6. It was clearly seen that the effect of NPs application on increasing the total concentrations of P without any pollutants additives resulted in an osculating in the reduction or increment of P in the plant. The order of sequence for the effects of NPs application on the increasing the total P was found to take the following sequence Si1 > Si2 > Mg1 > C (control) > Zn1 > Zn2 > Mg2. The highest values affected the increases of the available P were observed with Si1, whereas the lowest values were obtained when Mg2 was added. There was a significant difference between all treatment except for the treatments of (Si2 and Mg1). When Cu2+ was added to the soil as a pollutant to increase the original exit values by 5 mg kg−1, the effects of NPs application on the increment of total P were found to take the following order Zn1 > Si2 > C (control) > Si1 > Zn2 > Mg2 > Mg162. The highest value of the effects of adding NPs on the artificially polluted soils with Cu2+ (5 mg kg−1) to increase the total concentrations of P in the plant was found when Zn1 was added to the soil, whereas the lowest effect was found when Mg1 was added. There was a significant difference between all treatments. Increasing the values of an external addition of Cu2+ to 10 mg kg−1 resulted in changing the order of effects of NPs on increase the total concentrations of P in the plant to the following order Si1 > Zn1 > C (control) > Si2 > Mg1 > Mg2 > Zn2. There was a significant difference between all treatments. It was clearly seen that the highest effects in the three trials that were studied in the present work including the control, 5 mg kg−1, and 10 mg kg−1 were osculated among Si1, Zn1, and Si1, respectively. The effects of Cu2+ additives with two concentrations of 5 mg kg−1 and 10 mg kg−1 simultaneous with different treatments of NPs on increasing the total amounts of K in the plant are listed in Table 6. It was clearly seen that the effect of NPs applications on increasing the total concentrations of K without any Cu2+ additives were resulted in an osculating in the reduction or increment of total K in the plant. The order of sequence for the effects of NPs application on increasing the total K was found to take the following sequence Zn2 > C (control) > Mg1 > Mg2 > Si2 > Si1 > Zn1. The highest values affected the increases of the total N were observed with Zn2, whereas the lowest values were obtained when Zn1 was added. There was a significant difference between all treatments. When Cu2+ was added to the soil as an external pollutant to increase the original exit values by 5 mg kg−1, the effects of NPs application on the increment of total K were found to take the following order Si2 > Zn1 > Zn2 > Mg2 > Si1 > C (control) > Mg1. The highest values of the effects of adding NPs on the artificially polluted soils with Cu2+ (5 mg kg−1) to increase the total concentrations of K in the plant were found when Si2 was added to the soil, whereas the lowest effect was found when Mg1 was added. There was a significant difference between all treatments except for the treatments of (Z1 and Zn2). Increasing the values of Cu2+ to 10 mg kg−1 resulted in changing the order of effects of NPs on increase the total concentrations of K in the plant to the following order C (control) > Zn1 > Zn2 > Si2 > Mg1 > Si1 > Mg258,62. There was a significant difference between all treatments except for the following treatments (control and Zn1). It was clearly seen that the highest effects in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 were osculated among Zn2, Si2, and control, respectively.
Effect of Fe3+ additives and ZnO, MgO, and SiO2 NPs treatment on the accumulation of N, P, and K in the plant
The effects of Fe3+ additives with two concentrations of 5 mg kg−1 and 10 mg kg−1 simultaneously with different treatment of NPs on increasing the total amounts of N in the plant are listed in Table 6. It was clearly seen that the effect of NPs application on increasing the total concentrations of N without any pollutants additives resulted in an osculating in the reduction or increment of N in the plant. The order of sequence for the effects of NPs application on the increasing the total N was found to take the following sequence Mg2 > Zn2 > Si2 > C (control) > Mg1 > Si1 > Zn1. The highest values affected the increases of the total N were observed with Mg2, whereas the lowest values were obtained when Zn1 was added. There was a significant difference between all treatment except for the treatments of (Si1 and Mg1). When Fe3+ was added to the soil as an external addition to increase the original exit values by 5 mg kg−1, the effects of NPs application on the increment of total N were found to take the following order Si1 > C (control) > Mg1 > Si1 > Zn1 > Zn2 = Mg2. The highest value of the effects of adding NPs on the artificially polluted soils with Fe3+ (5 mg kg−1) to increase the total concentrations of N in the plant was found when Si1 was added to the soil, whereas the lowest effect was found when Mg2 was added. There was a significant difference between all treatments except for the treatments of (Zn2 and Mg2). Increasing the values of polluted Fe3+ to 10 mg kg−1 resulted in changing the order of effects of NPs on increase the total concentrations of N in the plant to the following order C (control) > Mg1 > Zn1 > Si2 > Zn2 > Si1 > Mg2. There was a significant difference between all treatments. It was clearly seen that the highest effects in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 were osculated among Mg2, Si1, and control, respectively. The effects of Fe3+ additives with two concentrations of 5 mg kg−1 and 10 mg kg−1 simultaneously with different treatment of NPs on increasing the total amounts of P in the plant are listed in Table 6. It was clearly seen that the effect of NPs application on increasing the total concentrations of P without any pollutants additives resulted in an osculating in the reduction or increment of P in the plant58. The order of sequence for the effects of NPs application on the increasing the total P was found to take the following sequence Si1 > Si2 > Mg1 > C (control) > Zn1 > Zn2 > Mg2 which is similar to what was observed with Cu2+ additives at the same concentrations. The highest values affected the increases of the total P were observed with Si1, whereas the lowest values were obtained when Mg2 was added. There was a significant difference between all treatments except for the treatments of (Si2 and Mg1). When Fe3+ was added to the soil as pollutant to increase the original exit values by 5 mg kg−1, the effects of NPs application on the increment of total P were found to take the following order Si2 > Si1 > Mg2 > Mg1 > Zn2 > C (control) > Si1 = Mg2. The highest values of the effects of adding NPs on the artificially polluted soils with Fe3+ (5 mg kg−1) to increase the total concentrations of P in the plant were found when Si2 was added to the soil, whereas the lowest effects were found when Mg2 were added. There was a significant difference between all treatments except for (control and Zn1) and (Zn2 and Mg1). Increasing the values of an external addition of Fe3+ to 10 mg kg−1 resulted in changing the order of effects of NPs on increasing the total concentrations of P in the plant to the following order Zn1 > Mg1 > Zn2 > Si2 > C (control) > Si1 = Mg262. There was a significant difference between all treatments. It was clearly seen that the highest effects in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 were osculated among Si1, Si2, and Zn1, respectively. The effects of Fe3+ additives with two concentrations of 5 mg kg−1 and 10 mg kg−1 simultaneously with different treatment of NPs on increasing the total amounts of K in the plant are listed in Table 6. It was clearly seen that the effect of NPs application on increasing the total concentrations of K without any pollutants additives resulted in an osculating in the reduction or increment of K in the plant. The order of sequence for the effects of NPs application on increasing the total K was found to take the following sequence Zn2 > C (control) > Mg1 > Mg2 > Si2 > Si1 > Zn1 which is similar to what was observed during Cu2+ additives at the same concentrations. The highest values affected the increases of the total K were observed with Zn2, whereas the lowest values were obtained when Zn1 was added. There was a significant difference between all treatments except for (control and Mg1). When Fe3+ was added to the soil as an external addition to increase the original exit values by 5 mg kg−1, the effects of NPs application on the increment of total K were found to take the following order Zn1 Mg2 > Si1 > Zn2 > C (control) > Mg1 > Si2. The highest value of the effects of adding NPs on the artificially polluted soils with Fe3+ (5 mg kg−1) to increase the total concentrations of K in the plant was found when Zn1 was added to the soil, whereas the lowest effect was found when Si2 was added. There was a significant difference between all treatments except for the treatments of (control and Mg1)58. Increasing the values of an external addition of Fe3+ to 10 mg kg−1 resulted in changing the order of effects of NPs on increase the total concentrations of K in the plant to the following order Si2 > Zn2 > C (control) > Zn1 > Si1 > Mg1 > Mg2. There was a significant difference between all treatments. It was clearly seen that the highest effects in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 were osculated among Zn2, Zn1, and Si2, respectively. The trend of these results agreed with those reported by Hegab et al.63,64 and Ali et al.61.
Effect of different ZnO, MgO, and SiO2 NPs and polluted water containing Cu2+ and Fe3+ solution on dry and wet weights of Marjoram plant.
Effect of different ZnO, MgO, and SiO2 NPs and polluted water containing Cu2+ on dry and wet weights of Marjoram plant
The effects of Cu2+ additives with different NPs treatments on dry and wet weights of Marjoram are presented in Table 7. The effects of two concentrations (5 mg kg−1 and 10 mg kg−1) of Cu2+ additives have been investigated. It was clearly seen that the effect of NPs application presented a negative effect on Marjoram dry weight in the experiments that have been carried out without Cu2+ additives. The order of sequence for the effects of NPs application on increasing the dry weight was found to take the following order control > Si2 = Mg1 > Si1 > Zn1 > Mg2 > Zn2. The highest values of means for dry weight were observed in the control treatment, whereas the lowest values were obtained when Zn2 was added. There was a significant difference between all treatments except for the treatments of (Si2 and Mg2)62. When Cu2+ was added to the soil as an external addition to increase the original exit values by 5 mg kg−1, the effects of NPs application on Marjoram dry weight took the following order Zn2 > Mg2 > Si2 > C (control) > Zn1 > Si1 > Mg1. The highest value of the effects of adding NPs on the artificially polluted soils with Cu2+ (5 mg kg−1) was found when Zn2 was added to the soil, whereas the lowest effect was found when Mg1 was added. There was a significant difference between all treatments except for the treatments of (control, Zn1, and Si2) and (Si1 and Mg1). Increasing the values of original exist values of Cu2+ by 10 mg kg−1 resulted in changing the order of effects of NPs on Marjoram dry weight to the following order Zn1 > Zn2 > Mg2 > Si2 > C (control) > Si1 Mg1. There was a significant difference between all treatments except for the treatments of (control, Si1, Si2 and Mg1) and (Zn2, Mg2). It was clearly seen that the highest effect in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 was relevant to the additives of control, Zn2, and Zn1, respectively. It was clearly seen that the effect of NPs application presented a negative effect on Marjoram wet weight in the experiments that have been carried out without Cu2+ additives. The order of sequence for the effects of NPs application on increasing the wet weight was found to take the following order control > Si2 = Mg1 > Si1 > Mg2 > Zn1 > Zn2. The highest values of means for wet weight were observed in the control treatment, whereas the lowest values were obtained when Zn2 was added which is similar to data that has been observed in dry weight. There was a significant difference between all treatments except for the treatments of Si2 and Mg1. When Cu2+ was added to the soil as an external pollutant to increase the original exiting values by 5 mg kg−1, the effects of NPs application on Marjoram wet weight took the following order Zn2 > Si1 = Mg2 > Zn1 = Mg1 > C (control) > Si2. The highest value of the effects of adding NPs on the artificially polluted soils with Cu2+ (5 mg kg−1) was found when Zn2 was added to the soil, whereas the lowest effect was found when Si2 was added. There was a significant difference between all treatments except for the treatments of control, Zn1, Si1, Mg1, and Mg2. Increasing the values of original exist values of Cu2+ addition by 10 mg kg−1 resulted in changing the order of effects of NPs on Marjoram wet weight to the following order Zn1 > Zn2 > C (control) > Mg1 > Si2 = Mg2 > Si1. There was a significant difference between all treatments except for the treatments of (control and Zn2) and (Si2, Mg1, and Mg2). It was clearly seen that the highest effects in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 were relevant to the additives of control, Zn2, and Zn1, respectively similar to what was observed in dry weight. The fresh and dry weights were affected by the use of Zn, Si, Mg NPs and may be the lower biomass in the control plants might be due to the higher Fe3+ and Cu2+ levels in these plants. These elements mediated reduction in plant growth might be associated with the disturbance of several mechanisms in plants such as chlorophyll biosynthesis, water deficit, and ultra-structural alteration in plant65. These results are in close conformity with Venkatachalam et al.66.
Effect of ZnO, MgO, and SiO2 NPs and polluted water containing Fe3+ on dry and wet weights of Marjoram plant
The effects of Fe3+ additives with different NPs treatments on dry and wet weights of Marjoram are presented in Table 7. The effects of two concentrations of 5 mg kg−1 and 10 mg kg−1 of Feon dry and wet weights of Marjoram plant have been investigated. It was clearly seen that the effect of NPs application presented a negative effect on Marjoram dry weight in the experiments that have been carried out without Fe3+ additives. The order of sequence for the effects of NPs application was found to take the following order C (control) > Si2 = Mg1 > Si1 > Zn1 > Mg2 > Zn2. The highest values of means for dry weight were observed in the control treatment, whereas the lowest values were obtained when Zn2 was added. There was a significant difference between all treatments except for the treatments of Si2 and Mg1. When Fe3+ was added to the soil as an external addition to increase the original exit values by 5 mg kg−1, the effects of NPs application on Marjoram dry weight took the following order Mg1 > Si1 > C (control) = Zn2 > Zn1 > Mg2 > Si2. The highest value of the effects of adding NPs on the artificially polluted soils with Fe3+ (5 mg kg−1) was found when Mg1 was added to the soil, whereas the lowest effect was found when Si2 was added. There was a significant difference between all treatments except for the treatments of (control and Zn2) and (Zn1, Si2, and Mg2)54,58. Increasing the values of original exist values of Fe3+ by 10 mg kg−1 resulted in changing the order of effects of NPs on Marjoram dry weight to the following order Mg1 > Si2 > C (control) = Zn2 = Mg2 > Zn1 > Si1. There was a significant difference between all treatment except for the treatments of (control, Zn2, and Mg2) and (Zn1 and Si1). It was clearly seen that the highest effects in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 were relevant to the additives of control, Mg1, and Mg1, respectively. It was clearly seen that the effect of NPs application presented a negative effect on Marjoram wet weight in the experiments that have been carried out without Fe3+ additives. The order of sequence for the effects of NPs application was found to take the following order C (control) > Si2 = Mg1 > Si1 > Mg2 > Zn1 > Zn2. The highest values of means for wet weight were observed in the control treatment, whereas the lowest values were obtained when Zn2 was added. There was a significant difference between all treatments except for the treatments of (Si2 and Mg1). When Fe3+ was added to the soil as an external addition to increase the original exit values by 5 mg kg−1, the effects of NPs application on Marjoram wet weight took the following order Mg1 > Si1 > control = Zn2 > Si2 > Zn1 > Mg2. The highest values of the effects of adding NPs on the artificially polluted soils with Fe3+ (5 mg kg−1) were found when Mg1 was added to the soil, whereas the lowest effect was found when Mg2 was added. There was a significant difference between all treatments except for the treatments of control and Zn2. Increasing the values of original exist values of Fe3+ by 10 mg kg−1 resulted in changing the order of effects of NPs on Marjoram wet weight to the following order Mg1 > Si2 > C (control) > Zn2 > Mg2 > Zn1 > Si1. There was a significant difference between all treatment except for the treatments of (Zn2 and Mg2). It was clearly seen that the highest effect in the three trials that were studied in the present work including control, 5 mg kg−1, and 10 mg kg−1 was relevant to the additives of control, Mg1, and Si2, respectively. These results are in close conformity with Tripathi et al.67 who reported that Supply of SiO2 NPs enhanced the photosynthetic pigments in Cr-stressed pea leaves.
Conclusion
In this study, we conducted a green synthesis of ZnO, MgO, and SiO2 NPs to investigate their effects on the quality of irrigation water, the availability of some heavy metals in soil and plants, and the productivity of marjoram. The results obtained from our experiments explored that the addition of NPs resulted in noticeable variations in the removal percentages of both Cu2+and Fe3+. The maximum values obtained for the adsorption of Cu2+ on ZnO, MgO, and SiO2 NPs within the pH values of 3–5 were 89.9%, 83.3%, and 68.36%, respectively. In contrast, the maximum adsorption values of Fe3+ at pH 3.3 were 82%, 80%, and 65% for the ZnO, MgO, and SiO2 NPs, respectively.
Whereas, the maximum adsorption values of Fe3+ at pH 3.3 were 82%, 80%, and 65% for ZnO, MgO, and SiO2 NPs, respectively. Whereas, the maximum adsorption values of Fe3+ at pH 3.3 were 82%, 80%, and 65% for ZnO, MgO, and SiO2 NPs, respectively. It was clearly seen that the effect of NPs application on the availability of substantial concentrations of Cu2+ without any pollutants additives resulted in the reduction of the available Cu2+ in the soil samples, and that same tendency was observed with the substantial concentrations of Fe exist in the soil. Adding NPs to the soil system had positive effects on Cu2+ uptake via the plant. The effect of NPs and the addition of Cu2+ and Fe3+ on the availability of NPK in the soil system were very completed and osculated from one treatment to another. The same tendency was observed with the total concentration of NPK in the plant. It was clearly seen that the effects of NPs application have presented a negative effect on Marjoram dry and wet weight in the experiments that have been carried out without the additions of either Cu2+ or Fe3+.
References
Singh, J. et al. The potential of green synthesized zinc oxide nanoparticles as nutrient source for plant growth. J. Clean. Prod. 214, 1061–1070 (2019).
Singh, J., Kumar, V., Kim, K. H. & Rawat, M. Biogenic synthesis of copper oxide nanoparticles using plant extract and its prodigious potential for photocatalytic degradation of dyes. Environ. Res. 177, 108569 (2019).
Malik, P., Shankar, R., Malik, V., Sharma, N., & Mukherjee, T. K. Green chemistry based benign routes for nanoparticle synthesis. J. Nanoparticles, 2014, 14 (2014).
Zhang, D., Ma, X. L., Gu, Y., Huang, H., & Zhang, G. W. Green synthesis of metallic nanoparticles and their potential applications to treat cancer. Front. Chem. 799, 1–18 (2020).
Singh, J. et al. ‘Green’synthesis of metals and their oxide nanoparticles: Applications for environmental remediation. J. Nanobiotechnol. 16, 1–24 (2018).
Jadoun, S., Arif, R., Jangid, N. K. & Meena, R. K. Green synthesis of nanoparticles using plant extracts: A review. Environ. Chem. Lett. 19(1), 355–374 (2021).
Singh, J. et al. Fabrication and characterization of barium based bioactive glasses in terms of physical, structural, mechanical and radiation shielding properties. Ceram. Int. 47, 21730–21743 (2021).
Gomez, A. et al. Effects of nano-enabled agricultural strategies on food quality: Current knowledge and future research needs. J. Hazard. Mater. 401, 123385 (2021).
Singh, J., Mehta, A., Rawat, M. & Basu, S. Green synthesis of silver nanoparticles using sun dried tulsi leaves and its catalytic application for 4-nitrophenol reduction. J. Environ. Chem. Eng. 6, 1468–1474 (2018).
Singh, K. et al. In situ green synthesis of Au/Ag nanostructures on a metal-organic framework surface for photocatalytic reduction of p-nitrophenol. J. Ind. Eng. Chem. 81, 196–205 (2020).
Singhal, G., Bhavesh, R., Kasariya, K., Sharma, A. R. & Singh, R. P. Biosynthesis of silver nanoparticles using Ocimum sanctum (Tulsi) leaf extract and screening its antimicrobial activity. J. Nanopart. Res. 13, 2981–2988 (2011).
Alagumuthu, G. & Kirubha, R. Green synthesis of silver nanoparticles using Cissus quadrangularis plant extract and their antibacterial activity. Int. J. Nanomater. Biostruct. 2, 30–33 (2012).
Singh, J. et al. Highly fluorescent carbon dots derived from Mangifera indica leaves for selective detection of metal ions. Sci. Total Environ. 720, 137604 (2020).
Liu, R. & Lal, R. Potentials of engineered nanoparticles as fertilizers for increasing agronomic productions. Sci. Total Environ. 514, 131–139 (2015).
Abdel-Aziz, H. M., Hasaneen, M. N. & Omer, A. M. Nano chitosan-NPK fertilizer enhances the growth and productivity of wheat plants grown in sandy soil. Span. J. Agric. Res. 14, e0902 (2016).
Adisa, I. O. et al. Recent advances in nano-enabled fertilizers and pesticides: A critical review of mechanisms of action. Environ. Sci. Nano 6, 2002–2030 (2019).
Chhipa, H. Nanofertilizers and nanopesticides for agriculture. Environ. Chem. Lett. 15, 15–22 (2017).
Abou-Shady, A., & El-Araby, H. Electro-agric, a novel environmental engineering perspective to overcome the global water crisis via marginal water reuse. Nat. Hazards Res. 1, 202–226 (2021).
Faria, D. et al. Sewage treatment using Aqueous Phase Reforming for reuse purpose. J. Water Process Eng. 37, 101413 (2020).
Ricart, S. & Rico, A. M. Assessing technical and social driving factors of water reuse in agriculture: A review on risks, regulation and the yuck factor. Agric. Water Manag. 217, 426–439 (2019).
López-Morales, C. A. & Rodríguez-Tapia, L. On the economic analysis of wastewater treatment and reuse for designing strategies for water sustainability: Lessons from the Mexico Valley Basin. Resour. Conserv. Recycl. 140, 1–12 (2019).
Inglese, P., & Sortino, G. Citrus history, taxonomy, breeding, and fruit quality. In Oxford Research Encyclopedia of Environmental Science, (2019).
Guimarães, R. et al. Targeting excessive free radicals with peels and juices of citrus fruits: Grapefruit, lemon, lime and orange. Food Chem. Toxicol. 48, 99–106 (2010).
Hama, D. M. & Mahmood, P. H. Characterization of antioxidant property and chemical composition of lemon (Citrus lemon L.) peel extracts. J. Raparin Univ. 3, 103 (2017).
Abou-Shady, A. Recycling of polluted wastewater for agriculture purpose using electrodialysis: Perspective for large scale application. Chem. Eng. J. 323, 1–18 (2017).
Abou-Shady, A. Reclaiming salt-affected soils using electro-remediation technology: PCPSS evaluation. Electrochim. Acta 190, 511–520 (2016).
Cottenie, A., Verloo, M., Kiekens, L., Velghe, G. & Camerlynck, R. Chemical Analysis of Plants and Soils (Lab. Agroch. State Univ., 1982).
Dahnke, W. C. & Johnson, G. V. Testing soils for available nitrogen. Soil Test. Plant Anal. 3, 127–139 (1990).
Soltanpour, P. N. Use of AB-DTPA soil test to evaluate element availability and toxicity. Commun. Soil Sci. Plant Anal. 16, 323–338 (1985).
Ietswaart, J. H. & Ietswaart, J. H. A Taxonomic Revision of the Genus Origanum (Labiatae) Vol. 4, 158 (Leiden University Press, 1980).
Turek, A., Wieczorek, K. & Wolf, W. M. Digestion procedure and determination of heavy metals in sewage sludge—An analytical problem. Sustainability 11, 1753 (2019).
Kotp, Y. H. Controlled synthesis and sorption properties of magnesium silicate nanoflower prepared by a surfactant-mediated method. Sep. Sci. Technol. 52, 657–670 (2017).
Ali, I. M., Nassar, M. Y., Kotp, Y. H. & Khalil, M. Cylindrical-design, dehydration, and sorption properties of easily synthesized magnesium phosphosilicatenanopowder. Part. Sci. Technol. 37, 207–219 (2019).
Jaiswal, V. et al. UV radiation protection by thermal plasma synthesized zinc oxide nanosheets. J. Inorg. Organomet. Polym Mater. 27, 1211–1219 (2017).
Suresh, D., Nethravathi, P. C., Rajanaika, H., Nagabhushana, H. & Sharma, S. C. Green synthesis of multifunctional zinc oxide (ZnO) nanoparticles using Cassia fistula plant extract and their photodegradative, antioxidant and antibacterial activities. Mater. Sci. Semicond. Process. 31, 446–454 (2015).
Shawky, H. A., Yaseen, R., Kotp, Y. H. & Eissa, D. Biosynthesis of silver nanoparticles and its effect on TFC RO membrane for groundwater desalination. Desalin. Water Treat. 193, 34–47 (2020).
Suresh, J., Pradheesh, G., Alexramani, V., Sundrarajan, M. & Hong, S. I. Green synthesis and characterization of hexagonal shaped MgO nanoparticles using insulin plant (Costuspictus D. Don) leave extract and its antimicrobial as well as anticancer activity. Adv. Powder Technol. 29, 1685–1694 (2018).
Suresh, J., Pradheesh, G., Alexramani, V., Sundrarajan, M. & Hong, S. I. Green synthesis and characterization of zinc oxide nanoparticle using insulin plant (Costuspictus D. Don) and investigation of its antimicrobial as well as anticancer activities. Adv. Nat. Sci. Nanosci. Nanotechnol. 9, 015008 (2018).
Zheng, Y. et al. Luminescence and photocatalytic activity of ZnO nanocrystals: correlation between structure and property. Inorg. Chem. 46, 6675–6682 (2007).
Mohapatra, P. et al. Calcination does not remove all carbon from colloidal nanocrystal assemblies. Nat. Commun. 8, 1–7 (2017).
Kotp, Y. H. High-flux TFN nanofiltration membranes incorporated with Camphor-Al2O3 nanoparticles for brackish water desalination. Chemosphere 265, 128999 (2021).
Kotp, Y. H. Enhancement of industrial effluents quality by using nanocomposite Mg/Al LDH ultrafiltration membranes”. J. Inorg. Organomet. Polym Mater. 30, 5244–5260 (2020).
Azam, A. et al. Antimicrobial activity of metal oxide nanoparticles against Gram-positive and Gram-negative bacteria: a comparative study. Int. J. Nanomed. 7, 6003 (2012).
El-Sakhawy, M., Adel, A. M., Diab, M. A. & Al-Shemy, M. Facile methods for the preparation of micro-and mesoporous amorphous silica from rice husk. Biomass Convers. Biorefinery 1–10 (2020).
El-Aassar, A. M., Abo ElFadl, M. M. S., Ali, M. E. A., Kotp, Y. H. & Shawky, H. A. Effect of manufacture conditions on reverse osmosis desalination performance of polyamide thin film composite membrane and their spiral wound element. Desalin. Water Treat. 69, 65–71 (2017).
Bayramoğlu, G. & Arıca, M. Y. Construction a hybrid biosorbent using Scenedesmusquadricauda and Ca-alginate for biosorption of Cu(II), Zn(II) and Ni(II): Kinetics and equilibrium studies. Bioresour. Technol. 100, 186–193 (2009).
Jain, P. K., Soni, A., Jain, P. & Bhawsar, J. Phytochemical analysis of Menthaspicata plant extract using UV-VIS, FTIR and GC/MS technique. J. Chem. Pharm. Res. 8, 1–6 (2016).
Dobrucka, R. Synthesis of MgO nanoparticles using Artemisia abrotanumherba extract and their antioxidant and photocatalytic properties. Iran. J. Sci. Technol. Trans. A Sci. 42, 547–555 (2018).
Park, J. T., Seo, J. A., Ahn, S. H., Kim, J. H. & Kang, S. W. Surface modification of silica nanoparticles with hydrophilic polymers. J. Ind. Eng. Chem. 16, 517–522 (2010).
Yang, C. H. Statistical mechanical study on the Freundlich isotherm equation. J. Colloid Interface Sci. 208, 379–387 (1998).
Jiang, J. Q., Cooper, C. & Ouki, S. Comparison of modified montmorillonite adsorbents: part I: Preparation, characterization and phenol adsorption. Chemosphere 47, 711–716 (2002).
Taha, M. R., Ahmad, K., Aziz, A. A., & Chik, Z. Geoenvironmental aspects of tropical residual soils. In Tropical Residual Soils Engineering, 391–420 (CRC Press, 2004).
Boparai, H. K., Joseph, M. & O’Carroll, D. M. Kinetics and thermodynamics of cadmium ion removal by adsorption onto nanozerovalent iron particles. J. Hazard. Mater. 186, 458–465 (2011).
An, H. K., Park, B. Y. & Kim, D. S. Crab shell for the removal of heavy metals from aqueous solution. Water Res. 35, 3551–3556 (2001).
Singh, D. B., Rupainwar, D. C., Prasad, G. & Jayaprakas, K. C. Studies on the Cd (II) removal from water by adsorption. J. Hazard. Mater. 60, 29–40 (1998).
Araújo, R., Castro, A. C. M. & Fiúza, A. The use of nanoparticles in soil and water remediation processes. Mater. Today Proc. 2, 315–320 (2015).
Baragaño, D., Forján, R., Welte, L. & Gallego, J. L. R. Nanoremediation of As and metals polluted soils by means of graphene oxide nanoparticles. Sci. Rep. 10, 1–10 (2020).
Javed, H., Naeem, A., Rengel, Z. & Dahlawi, S. Timing of foliar Zn application Plays a vital role in minimizing Cd accumulation in wheat. Environ. Sci. Pollut. Res. 23, 16432–16439 (2016).
Hussain, A. et al. Zinc oxide nanoparticles alter the wheat physiological response and reduce the cadmium uptake by plants. Environ. Pollut. 242, 1518–1526 (2018).
Wang, H. et al. Foliar application of Zn can reduce Cd concentrations in rice (Oryza sativa L.) under field conditions. Environ. Sci. Pollut. Res. 25, 29287–29294 (2018).
Ali, S. et al. Combined use of biochar and zinc oxide nanoparticle foliar spray improved the plant growth and decreased the cadmium accumulation in rice (Oryza sativa L.) plant. Environ. Sci. Pollut. Res. 26, 11288–11299 (2019).
Pandey, V. C. Phytoremediation of heavy metals from fly ash pond by Azollacaroliniana. Ecotoxicol. Environ. Saf. 82, 8–12 (2012).
Hagab, R. H., Kotp, Y. H. & Eissa, D. Using nanotechnology for enhancing phosphorus fertilizer use efficiency of peanut bean grown in sandy soils. J. Adv. Pharm. Educ. Res. 8, 59–67 (2018).
Hegab, R., Abou Batta, W. & El-Shazly, M. Effect of mineral, nano and bio nitrogen fertilization on nitrogen content and productivity of Salvia officinalis L. plant. J. Soil Sci. Agric. Eng. 9, 393–401 (2018).
Ali, B. et al. 5-Aminolevolinic acid mitigates the cadmium-induced changes in Brassica napus as revealed by the biochemical and ultra-structural evaluation of roots. Ecotoxicol. Environ. Saf. 92, 271–280 (2013).
Venkatachalam, P. et al. Zinc oxide nanoparticles (ZnONPs) alleviate heavy metal-induced toxicity in Leucaena leucocephala seedlings: A physiochemical analysis. Plant Physiol. Biochem. 110, 59–69 (2017).
Tripathi, D. K., Singh, V. P., Prasad, S. M., Chauhan, D. K. & Dubey, N. K. Silicon nanoparticles (SiNp) alleviate chromium (VI) phytotoxicity in Pisum sativum (L.) seedlings. Plant Physiol. Biochem. 96, 189–198 (2015).
Acknowledgements
All authors would like to thank the Desert Research Center (DRC)—Egypt for its financial support.
Funding
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB). This research did not receive any specific grant from funding agencies in the public, commercial, or not-for-profit sectors.
Author information
Authors and Affiliations
Contributions
Authors D.E. , Y.H.K. and A.A.S. wrote the main manuscript text and authors R.H.H. and Y.H.K. prepared figures and tables and all authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Eissa, D., Hegab, R.H., Abou-Shady, A. et al. Green synthesis of ZnO, MgO and SiO2 nanoparticles and its effect on irrigation water, soil properties, and Origanum majorana productivity. Sci Rep 12, 5780 (2022). https://doi.org/10.1038/s41598-022-09423-2
Received:
Accepted:
Published:
Version of record:
DOI: https://doi.org/10.1038/s41598-022-09423-2
This article is cited by
-
A Green Synthesis by Pulse Laser Ablation in Liquid to Form Pd@TiO2@SiO2 Core@Shell Nanoparticles for High-Performance Antibacterial and Antioxidant Agents
BioNanoScience (2026)
-
Bioharvesting and improvement of nano-silica yield from bagasse by irradiated Curvularia spicifera
BMC Microbiology (2025)
-
Silica nanoparticles from agave distillate for the removal of the Methylene Blue dye from water
Journal of Materials Science: Materials in Engineering (2025)
-
Use of the sunscreen for the degradation of a toxic methyl blue dye with hydrogen peroxide
Scientific Reports (2025)
-
Novel approach to enhance antifungal properties via formation of wavy and Sharp microstructures composed of metal oxide nanoparticles and Cdots
Scientific Reports (2025)