Fig. 6

Mean distance between plane defects (twinning planes) forming during crystallization in the direction \(\left[ 111\right]\) in \(\sim 12~{\text {nm}} \times \sim 12~{\text {nm}} \times \sim 630~{\text {nm}}\) samples vs. degree of overcooling.