Table 4 Crystalline sizes for all the plasma printed AgNP conductive structures on PDMS. The patterns are presented for different plasma voltages (0, 11, 14, 17, and 20 kV).

From: Plasma-aided direct printing of silver nanoparticle conductive structures on polydimethylsiloxane (PDMS) surfaces

Samples

2 θ

FWHM

Crystalline size D (nm)

Average crystalline size D (nm)

Crystallinity of the material (%)

AgNPs—0 kV (Dip Coating)

37.08763

0.62729

13.35799731

15.48024

10.65

43.22392

1.22152

6.995387852

63.58685

0.52123

17.93207882

76.60461

0.42831

23.63549498

AgNPs—11 kV (Plasma printing)

37.09807

0.63442

13.20827568

11.71685

22.05

43.25343

1.14929

7.435789338

63.59754

0.70016

13.35020281

76.61356

0.78644

12.87312879

AgNPs—14 kV (Plasma printing)

37.09415

0.59614

14.05625873

12.52977

22.78

43.26219

1.02725

8.319432826

63.59464

0.66038

14.15417085

76.61778

0.74502

13.58921631

AgNPs—17 kV (Plasma printing)

37.08829

0.60938

13.75062247

12.23916

23.12

43.25027

1.06637

8.01390221

63.5912

0.67342

13.87983338

76.61405

0.7605

13.3122651

AgNPs—20 kV (Plasma printing)

37.11359

0.44773

18.7165818

17.00257

24.60

43.31112

0.66879

12.78067179

63.59972

0.49836

18.75629717

76.62693

0.5702

17.75671108