Table 2 Input-output parameters (experimental data) in this study.

From: Quality optimization of liquid silicon lenses based on sequential approximation optimization and radial basis function networks

Group

Melt temperature (°C)

Filling time (s)

Curing time (s)

Curing pressure (MPa)

Mold temperature (°C)

AverageVon-Mises thermal stress (Mpa)

Volume Shrinkage(%)

1

1.76

23.17

19.06

20.34

154.52

21.27

4.97

2

2.44

29.77

15.48

33.60

153.70

21.32

3.75

3

1.89

22.17

15.23

26.63

150.43

24.42

4.18

4

1.93

29.06

19.29

36.12

152.52

18.33

3.74

5

2.04

20.73

16.50

29.07

165.83

22.97

4.05

6

2.16

21.23

16.90

25.09

163.56

22.76

4.42

7

2.21

26.14

16.60

19.18

164.19

23.01

4.96

8

2.30

23.97

17.56

30.76

168.79

21.02

4.04

9

1.98

28.45

18.26

24.64

159.56

20.34

4.63

10

2.38

24.13

17.21

17.52

155.85

22.64

5.14

11

1.75

27.09

17.34

15.65

169.87

22.99

5.34

12

2.11

21.76

15.76

22.09

161.62

24.26

4.60

13

2.34

20.33

19.65

37.34

166.18

19.12

3.59

14

1.81

25.75

17.85

23.08

157.83

21.65

4.69

15

1.60

28.83

16.23

28.18

158.62

22.28

4.19

16

1.56

27.84

18.01

16.73

151.72

22.18

5.27

17

2.07

22.71

19.82

39.22

156.88

18.53

3.46

18

2.47

26.93

18.77

32.43

160.10

19.16

4.00

19

1.66

24.89

15.69

33.89

167.20

22.99

3.66

20

1.52

25.26

18.59

37.79

162.22

19.69

3.52

Back to article page